Physical-mechanical performance of the concrete produced with fiber addition jute plant in the partial replacement of Portland cement in 0.5% and 1.0%
Journal of Engineering and Technology for Industrial Applications
Physical-mechanical performance of the concrete produced with fiber addition jute plant in the partial replacement of Portland cement in 0.5% and 1.0%
Autor Correspondente: Bianka Caroline Cunha Firmino | [email protected]
Palavras-chave: concrete, jute fiber, potland cement.
Resumos Cadastrados
Resumo Português:
Este trabalho apresenta um estudo da viabilidade de utilização das fibras de Juta (Corchurus capsularis) como reforço na substituição parcial do cimento Portland em concreto convencional com fck de 25 MPa. Para isso, durante as etapas do estudo, foram realizados inúmeros ensaios laboratoriais com a finalidade de caracterizar os materiais empregados nesta pesquisa, tanto para os agregados miúdo e graúdo quanto para o cimento Portland e as fibras propostas. O objetivo após a caracterização dos materiais foi investigar o comportamento físico e mecânico dos corpos de prova de concreto moldados para as análises de ruptura aos 7 e 28 dias de cura e de absorção de água, divididos em três grupos diferentes, uma moldagem sendo o piloto com 0,0% de adição das fibras denominado como referência e outros dois com diferentes porcentagens extraídas do consumo de cimento total utilizado nos corpos de prova de concreto em análise, sendo o grupo 2 com 0,5% e o grupo 3 com 1,0% de fibra.
Resumo Inglês:
This work presents a feasibility study of the use of Jute fibers (Corchurus capsularis) as reinforcement in the partial replacement of Portland cement in conventional concrete with fck of 25 MPa. For this, during the study stages, numerous laboratory tests were carried out with the purpose of characterizing the materials used in this research, both for the small aggregates and for the Portland cement and the proposed fibers. The objective after the characterization of the materials was to investigate the physical and mechanical behavior of the concrete specimens molded for the analysis of rupture at 7 and 28 days of curing and water absorption, divided into three different groups, a molding being the pilot with 0.0% addition of fibers denominated as reference and another two with different percentages extracted from the consumption of total cement used in concrete test specimens under analysis, being group 2 with 0.5% and group 3 with 1, 0% fiber.